Properties
Liquidity: Casting resin has good fluidity, ensuring the integrity and accuracy of the casting.
Adhesion: Casting resin can adhere to the surface of the casting, forming a uniform coating, improving the surface of the casting and reducing defects.
High temperature resistance: In high temperature environments, the casting resin can maintain stability without thermal decomposition or melting, ensuring the smooth progress of the casting process
WASHlNG (Total cleaning time should not exceed 5min)
1.The reusable alcohol is filtered through a 200 mesh filter bag before each cleaning operation to ensure the
cleanliness of the alcohol.
2.Soak the platform and model together into clean 95% alcohol, set the cleaning machine working time for 2min
and wait for the resin attached to the surface of the model to be rinsed clean.
3.Put the platform and model into clean 95% alcohol again, set the cleaning machine working time for 2min, and
wait for the model to be cleaned.
4.Remove the model from the platform and blow out the alcohol on the surface with compressed air, then leave
it in a cool place until it is completely dry.
CURING
This material in the printing of small parts and no complex details of the model can choose to directly
embedded gypsum into the casting process, if the model surface has more uneven grooves or large pieces ot
the model in order to ensure the casting effect, it is recommended to carry out the post-curing, post-curino
operation process is as follows.
wil be thoroughly dried model placed into the LED-type curing box, curing time of 30min, if you find that the
model has a deformation in the curing process lf the model is found to be deformed during the curing process
then the model can be put into clean water for post-curing operation.
| Product Attribute Parameter Table | ||||
| model | RS-ALBINO | RS-AURORA | RS-OBSIDIAN | RS-OLIVE |
| Color | Transparent yellow | Orange (color) | Translucent Black | Greener |
| Viscosity | 450~550cps(25°C) | 250~350CPS | 250~350CPS | 1500cps~2000cps |
| Density | 1.06~1.075g/cm3 | 1.07~1.1g/cm3 | 1.07~1.1g/cm3 | 401500cps~2000cps |
| identity | Specialized resin materials designed for 3D printed jewelry casting | Can be used to print filigree models and can be dewaxed using the same heat-up curve as conventional waxes. | ||
| Recommended printing parameters | ||||
| model | RS-ALBINO | RS-AURORA | RS-OBSIDIAN | RS-OLIVE |
| Floor height | 0.05mm | 0.05mm | 0.05mm | 0.05mm |
| Layer exposure time | 3.5s~5.5s | 3.5s~5.5s | 3.5s~5.5s | 5.5s~6.5s |
| Bottom exposure time | 15s~25s | 15s~25s | 15s~25s | 40S |
| release film | ACF | ACF | ACF | ACF |
| Bottom level number | 6 | 6 | 6 | 6 |
| Transition layers | 10 | 10 | 10 | 10 |
| Static time after lifting | 2S | 2S | 2S | 2S |
| Rest time return journey | 2S | 2S | 2S | 2S |
Technical InformationModel:Z.M.CM.DVC-LPower supply:380V,50/60HZPower output:25KWSuitablemetal:Gold, Silver, CopperMelti···
MAIN FEATURE:1.High-powered intermediate frequency power supply is heated, andheating can automatically stir the molten ···
After finish melting, the sheet metal is made by high-speed centrifu-gation and rolling the sheet to make a sheet metal ···
1.DF Series Gold melting machine is a digital induction heating power supply [registered trademark DSPWER*]:2.The heatin···
Technical InformationModel：M.PR.VAN70-16KPrint Size：L211x W118 xH180mmPower Supply：110V/220V 50/60Hz 500WPrinting spe···
WASHING1.After the model has been printed, it needs to be left to bleed off as much of the resin as possible2.Use clean ···
WASHING1.The reusable alcohol is filtered through a 200 mesh filter bag before each cleaning operation to ensure theclea···
The High-Efficiency Vacuum Mixer Machine revolutionizes precision casting with its one-step operation. Designed for rapi···
The High-Efficiency Vacuum Mixer Machine revolutionizes precision casting with its one-step operation. Designed for rapi···
Applies toJewelry processing stores that deal with gold and silver jewelry.Jewelry processing factories engaged in large···
online serviceScan to wechat :